Impact Copolymer Polypropylene
Description
CPP 03900.NB features excellent impact resistance, good mold release, antistatic and processing properties, and no break impact copolymer.
Property
Value
Unit
ASTM
Melt index (condition 230°C/2.16 kg)
12
g/10 min
D 1238
Density (g/cm³)
0.900
g/cm³
D 792
Tensile Strength at Yield (2in/min; 50mm/min)
3400
psi
D638
Tensile Elongation at Yield
5
%
D638
Flexural Modulus – 1% Secant (0.05 in/min; 1 mm/min)
170,000
psi
D790A
Notched Izod Impact (73°F/23°C, Method A)
No Breaks
D256A
Deflection Temperature Under Load at 66psi, Unannealed
90
°C
D648
Vicat Softening Temperature
148
°C
D1525