Description
SHE150 resin is a High Density Polyethylene that has been specially designed for monofilament extrusion process and provides a good balance of processability, spinnability, knotting strength as well as a very low gels amount. It can also be blended with LLDPE to improve blown film stiffness. It contains processing aid and an oxidant additives. The minimum biobased carbon content of this grade is 94%, determined according to ASTM D6866.
Property
Value
Unit
ASTM
Melt index (condition 230°C/2.16 kg)
1
g/10 min
D 1238
Density (g/cm³)
0.948
g/cm³
D 792
Tensile Strength at Yield (a)
28
MPa
D 638
Tensile Strength at Break (a)
40
MPa
D 638
Flexural Modulus ‐ 1% Secant (b)
1280
MPa
D 2240
Shore D Hardness (c)
62
-
D 2240
Deflection Temperature under Load at 0.455 MPa (b)
76
ºC
D 648
Vicat Softening Temperature at 10 N (b)
128
ºC
D 1525